Phase relations at 850 and 870 C, melting transitions in air, oxygen, and helium were studied for Bi(2.1)Sr(1.9) CuO6 and for the Bi2Sr2Ca(n-1) Cu(n)O(2n+4) for n = 1, 2, 3, 4, 5, and infinity (CaCuO2). Up to 870 C, the n = 2 composition resides in the compatibility tetrahedron bounded by Bi(2+x)(Sr,Ca)(3-y) Cu2O8, (Sr,Ca)14 Cu24O41, Ca2CuO3, and a Bi-Sr-Ca-O phase. The n is greater than or equal to 3 compositions reside in the compatibility tetrahedron Bi(2+x)(Sr,Ca)(3-y) Cu2O8 - (Sr,Ca)14 Cu24O41 - Ca2CuO3 - CuO up to 850 C. However, Bi(2+x)Sr(4-y) Cu3O10 forms for n is greater than or equal to 3 after extended heating at 870 C. Bi(2+x)Sr(2-y) CuO6 and Bi(2+x)(Sr,Ca)(3-y) Cu2O8 melt in air at 914 C and 895 C respectively. During melting, all of the compositions studied lose 1 to 2 percent by weight of oxygen from the reduction of copper. Bi(2+x)Sr(2-y) CuO6, Bi(2+n)(Sr,Ca)(3-y) Cu2O8, and Bi(2+x)(Sr,Ca)(4-y) Cu3O10 exhibit crystallographic alignment in a magnetic field, with the c-axes orienting parallel to the field.